描述：
白剛玉是以優質氧化鋁為原料，在電弧爐中經2000℃以上熔化並冷卻而成。呈白色，主晶相α-Al2O3。
典型化學分析 [%]：
| 三氧化二鋁 | 三氧化二鐵 | 二氧化矽 | 氧化亞鐵 | 氧化鎂 | 高的 | 二氧化鈦 | 氧化鈉 | 氧化鉀 | 法律 |
| 99.5 | 0.04 | 0.01 | / | 0.01 | 0.01 | / | 0.25 | 0.01 | < 0.09 |
物理性能：
| 比重 | 硬度 | 晶型 | 熔點 |
| 3.96克/立方厘米 | 9.0莫氏標度 | 阿爾法氧化鋁 | 2050年 |
粒徑分佈：
| F8 | +4000um | 0 | +2800um | ≤20% | +2360um | ≥45% | +2360+2000um | ≥70% | -1700微米 | ≤3% |
| F10 | +3350um | 0 | +2360um | ≤20% | +2000um | ≥45% | +2000+1700um | ≥70% | -1400微米 | ≤3% |
| F12 | +2800um | 0 | +2000um | ≤20% | +1700um | ≥45% | +1700+1400um | ≥70% | -1180um | ≤3% |
| F14 | +2360um | 0 | +1700um | ≤20% | +1400um | ≥45% | +1400+1180um | ≥70% | -1000微米 | ≤3% |
| F16 | +2000um | 0 | +1400um | ≤20% | +1180um | ≥45% | +1180+1000um | ≥70% | -850微米 | ≤3% |
| F20 | +1700um | 0 | +1180um | ≤20% | +1000um | ≥45% | +1000+850um | ≥70% | -710微米 | ≤3% |
| F22 | +1400um | 0 | +1000um | ≤20% | +850um | ≥45% | +850+710um | ≥70% | -600微米 | ≤3% |
| F24 | +1180um | 0 | +850um | ≤25% | +710um | ≥45% | +710+600um | ≥65% | -500微米 | ≤3% |
| F30 | +1000um | 0 | +710um | ≤25% | +600um | ≥45% | +600+500um | ≥65% | -425微米 | ≤3% |
| F36 | +850um | 0 | +600um | ≤25% | +500微米 | ≥45% | +500+425um | ≥65% | -355微米 | ≤3% |
| F46 | +600um | 0 | +425微米 | ≤30% | +355微米 | ≥40% | 355+300um | ≥65% | -250微米 | ≤3% |
| F54 | +500微米 | 0 | +355微米 | ≤30% | +300微米 | ≥40% | +300+250um | ≥65% | -212微米 | ≤3% |
| F60 | +425微米 | 0 | +300微米 | ≤30% | +250微米 | ≥40% | 250+212微米 | ≥65% | -180um | ≤3% |
| F70 | +355微米 | 0 | +250微米 | ≤25% | +212微米 | ≥40% | +212+180um | ≥65% | -150微米 | ≤3% |
| F80 | +300微米 | 0 | +212微米 | ≤25% | +180微米 | ≥40% | +180+150um | ≥65% | -125微米 | ≤3% |
| F90 | +250微米 | 0 | +180微米 | ≤20% | +150微米 | ≥40% | +150+125um | ≥65% | -106奈米 | ≤3% |
| F100 | +212微米 | 0 | +150微米 | ≤20% | +125微米 | ≥40% | +125+106um | ≥65% | -75微米 | ≤3% |
| F120 | +180微米 | 0 | +125微米 | ≤20% | ≥40% | ≥40% | +106+90um | ≥65% | -63微米 | ≤3% |
| F150 | +150微米 | 0 | +106 | ≤15% | +75微米 | ≥40% | +75+63um | ≥65% | -45微米 | ≤3% |
| F180 | +125微米 | 0 | +90um | ≤15% | +75微米 | * | +75+63um | ≥40% | -53微米 | * |
| F220 | +106 | 0 | +75微米 | ≤15% | +63微米 | * | +63+53um | ≥40% | -45微米 | * |
應用：
-固結磨俱及塗附磨俱
-濕式和乾式噴砂介質、研磨和拋光等
-地板/牆壁層壓板
-熱噴塗/等離子噴塗
-陶瓷瓷磚、陶瓷過濾板、陶瓷膜等
-砂輪、杯形砂輪、油石、拋光墊等
-催化劑載體
-噴砂清理.表面處理
– 在玻璃上形成霧面效果
-去毛刺
-加工非常硬的部件
-金屬表面粗糙化
-耐磨