24 粒度白剛玉 WFA WA 磨料顆粒白色氧化鋁用於噴砂
白剛玉是以優質氧化鋁為原料，在電弧爐中2000℃以上高溫熔煉冷卻而成，呈白色，主晶相為α-Al 2 O 3，用電弧爐熔煉生產的白剛玉體積密度大，氣孔率低，可提高體積穩定性和抗熱震性。
物理特性
| 比重 | 3.96克/立方厘米 |
| 莫氏硬度 | 9.0 |
| 晶體形式 | α-氧化鋁 |
| 熔點 | 2250℃ |
典型化學分析[%]
| 氧化鋁 | 氧化鐵 | 氧化鐵 | 氧化鎂 | 高的 | 二氧化鈦 | 氧化鈉 | 氧化鉀 | 法律 |
| 99.5 | 0.04 | / | 0.01 | 0.01 | / | 0.25 | 0.01 | < 0.09 |
粒徑分佈
| F8 | +4000微米 | 0 | +2800微米 | ≤20% | +2360微米 | ≥45% | +2360+2000微米 | ≥70% | -1700微米 | ≤3% |
| F10 | +3350微米 | 0 | +2360微米 | ≤20% | +2000微米 | ≥45% | +2000+1700微米 | ≥70% | -1400微米 | ≤3% |
| F12 | +2800微米 | 0 | +2000微米 | ≤20% | +1700微米 | ≥45% | +1700+1400微米 | ≥70% | -1180微米 | ≤3% |
| F14 | +2360微米 | 0 | +1700微米 | ≤20% | +1400微米 | ≥45% | +1400+1180微米 | ≥70% | -1000微米 | ≤3% |
| F16 | +2000微米 | 0 | +1400微米 | ≤20% | +1180微米 | ≥45% | +1180+1000微米 | ≥70% | -850微米 | ≤3% |
| F20 | +1700微米 | 0 | +1180微米 | ≤20% | +1000微米 | ≥45% | +1000+850微米 | ≥70% | -710微米 | ≤3% |
| F22 | +1400微米 | 0 | +1000微米 | ≤20% | +850微米 | ≥45% | +850+710微米 | ≥70% | -600微米 | ≤3% |
| F24 | +1180微米 | 0 | +850微米 | ≤25% | +710微米 | ≥45% | +710+600微米 | ≥65% | -500微米 | ≤3% |
| F30 | +1000微米 | 0 | +710微米 | ≤25% | +600微米 | ≥45% | +600+500微米 | ≥65% | -425微米 | ≤3% |
| F36 | +850微米 | 0 | +600微米 | ≤25% | +500微米 | ≥45% | +500+425微米 | ≥65% | -355微米 | ≤3% |
| F46 | +600微米 | 0 | +425微米 | ≤30% | +355微米 | ≥40% | 355+300微米 | ≥65% | -250微米 | ≤3% |
| F54 | +500微米 | 0 | +355微米 | ≤30% | +300微米 | ≥40% | +300+250微米 | ≥65% | -212微米 | ≤3% |
| F60 | +425微米 | 0 | +300微米 | ≤30% | +250微米 | ≥40% | 250+212微米 | ≥65% | -180微米 | ≤3% |
| F70 | +355微米 | 0 | +250微米 | ≤25% | +212微米 | ≥40% | +212+180微米 | ≥65% | -150微米 | ≤3% |
| F80 | +300微米 | 0 | +212微米 | ≤25% | +180微米 | ≥40% | +180+150微米 | ≥65% | -125微米 | ≤3% |
| F90 | +250微米 | 0 | +180微米 | ≤20% | +150微米 | ≥40% | +150+125微米 | ≥65% | -106微米 | ≤3% |
| F100 | +212微米 | 0 | +150微米 | ≤20% | +125微米 | ≥40% | +125+106微米 | ≥65% | -75微米 | ≤3% |
| F120 | +180微米 | 0 | +125微米 | ≤20% | ≥40% | ≥40% | +106+90微米 | ≥65% | -63微米 | ≤3% |
| F150 | +150微米 | 0 | +106微米 | ≤15% | +75微米 | ≥40% | +75+63微米 | ≥65% | -45微米 | ≤3% |
| F180 | +125微米 | 0 | +90微米 | ≤15% | +75微米 | * | +75+63微米 | ≥40% | -53微米 | * |
| F220 | +106微米 | 0 | +75微米 | ≤15% | +63微米 | * | +63+53微米 | ≥40% | -45微米 | * |
主要應用
-固結磨俱及塗附磨俱
-在玻璃上形成霧面效果
-乾濕噴砂介質、研磨和拋光等
-地板/牆壁層壓板，耐磨
-熱噴塗/等離子噴塗，處理非常堅硬的部件
-催化劑載體
-陶瓷和瓷磚、陶瓷過濾板、陶瓷膜等
-砂輪、杯形砂輪、油石、拋光墊等
-噴砂清理、表面處理、去毛邊、金屬表面粗化